The frequency and energy dissipation change of a quartz crystal microbalance during moisture absorption was measured for films with thickness ranging from 3 to 205 nm. Evidence of the viscoelastic nature of the films was observed for films thicker than 90 nm through the frequency and energy dissipation changes. For sufficiently thin films (t < 40 nm), the frequency change could be effectively modeled as a simple increase in mass, as predicted by the Sauerbrey equation. The viscosity of the swollen films was independent of initial polymer film thickness (93-205 nm).